| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 基本性能 | 熔融指數 | 200℃/5kg | ASTM D-1238 | 3.0 | g/10min |
| 物理性能 | 比重 | ASTM D-792 | 1.05 | ||
| 模具收縮率 | ASTM D-955 | 0.4-0.7 | % | ||
| 機械性能 | 拉伸強度 | 50mm/min | ASTM D-638 | 500 | kg/cm2 |
| 伸長率 | 50mm/min | ASTM D-638 | 30 | % | |
| 抗彎強度 | 15mm/min | ASTM D-790 | 800 | kg/cm2 | |
| 抗彎模數 | 15mm/min | ASTM D-790 | 23000 | kg/cm2 | |
| IZOD缺口沖擊強度 | Notched 1/4" | ASTM D-256 | 17 | kg.cm/cm | |
| IZOD缺口沖擊強度 | Notched 1/8" | ASTM D-256 | 19 | kg.cm/cm | |
| 洛氏硬度 | ASTM D-785 | 100 | R-scale | ||
| 熱性能 | 熱變形溫度 | 18.5kg/cm21/2" | ASTM D-648 | 111 | ℃ |
| 維卡軟化點 | 1000g | ASTM D-1525 | 130 | ℃ | |
| 阻燃等級 | 1/8" | UL94 | HB | ||
| 阻燃等級 | 1/16" | UL94 | HB | ||